- Recrystallization Texture of Cold-Rolled 50-Iron 50-Nickel Alloy
- 50 Fe-Ni ゴウキン アツエンバン ノ サイケッショウ シュウゴウ ソシキ
この論文をさがす
抄録
Variations in the integrated intensities of (111), (200), (220) and (113) diffraction lines and in the intensities of the various areas of the (200) pole figure on annealing cold-rolled 50-Fe 50-Ni alloy were observed by an X-ray diffractometer. Prior to the primary recrystallization, sharpening of the cold-rolling texture is observed, probably caused by the polygonization. Initial growth of the cube-oriented recrystallized grains occurs without any appreciable decrease in the intensities of the areas near the poles of (110)[\bar112], (112)[11\bar1] and near-(123)[1\bar21] orientations in the (200) pole figure, during which the back-ground intensities around the poles of (100)[001] orientation are conspicuously lowered. The results show that the nuclei of the cube-oriented recrystallized grains are formed by the Burgers-Cahn mechanism in the local curvature of the cube-oriented deformed matrix.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 23 (6), 343-347, 1959
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681458576000
-
- NII論文ID
- 130007333524
- 40018257442
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9152882
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可