- 佐藤 史郎
- 住友軽金属工業株式会社研究部
書誌事項
- タイトル別名
-
- On the Corrosion of Copper-Nickel Base Alloys by Water and Steam at Elevated Temperature. (Corrosion of Copper Alloys in Hot Water and Steam. (5))
- コウオン コウアツ ノ ミズ オヨビ ジョウキ ニ ヨル ドウ-ニッケルキ ゴウキン ノ フショク ニ ツイテ
この論文をさがす
抄録
An investigation has been made to determine the corrosion resistance of binary and commercial copper-nickel base alloys in water and steam at elevated temperature. The tests were conducted by exposing the specimens to degassed or oxygen bearing water and steam at 200° to 350°C under saturated pressure for 250 hours. The results obtained were as follows: (1) In perfectly degassed condition, corrosion by water and steam increased with increasing of nickel content of alloys, but no severe corrosion was observed. (2) In oxygen bearing condition, severe corrosion of exfoliating, pitting, or intergranular type was observed on Cu-10∼90%Ni alloys except Monel metal by exposure to water and steam at 300° or 350°C. The exfoliating corrosion which was observed in above test was similar to that we have ever experienced in 70-30 cupronickel tubes used in feed water heater of power plant. (3) It is considered that severe corrosion by oxygen bearing water or steam at elevated temperature is due to the action of hydrogen gas which is evolved at the metal surface by selective oxidizing reaction of water and steam to exfoliate the oxide film. (4) Corrosion resistance of Monel metal containing 1.24% of iron to oxygen bearing water and steam is superior to that of binary alloys. This fact shows that iron is effective to form the protective films.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 27 (3), 134-139, 1963
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681458578048
-
- NII論文ID
- 130007333528
- 40018258232
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153672
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可