- Other Title
-
- 加工した銅の焼鈍による内部摩擦の変化について
- カコウ シタ ドウ ノ ショウドン ニ ヨル ナイブ マサツ ノ ヘンカ ニ ツイテ
Search this article
Description
Cold-rolled tough pitch copper and oxygen free copper were annealed for 1 hr at each of the following temperatures successively, namely, 20°, 100°, 158° (165°), 210°, 250°, 300° (308°), 367°, 443°, 518°, 600°, 700°C (temperatures in parentheses refer to oxygen free copper). Then the internal friction and its amplitude dependence were measured after each annealing at room temperature by the transversely vibrating bar method. The results were as following. (1) Before recrystallization, the internal friction was decreased with the annealing temperature and was independent of amplitude. (2) As recrystallization proceeded, a maximum developed in the internal friction-amplitude curve and the internal friction itself was much increased. These facts were inferred to be associated with birth of dislocations liberated from firm pins in the course of the recrystallization. (3) After annealing at higher temperatures than recrystallization completion temperature, both the internal friction and its amplitude dependence of oxygen-free copper were again decreased. This was looked upon as due to the concentration of impurities to the new-born dislocations.
Journal
-
- Journal of the Japan Institute of Metals and Materials
-
Journal of the Japan Institute of Metals and Materials 23 (7), 389-392, 1959
The Japan Institute of Metals and Materials
- Tweet
Details 詳細情報について
-
- CRID
- 1390282681458590592
-
- NII Article ID
- 130007333555
- 40018257472
-
- NII Book ID
- AN00062446
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL BIB ID
- 9152912
-
- Data Source
-
- JaLC
- NDL Search
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed