- Internal Friction Measurements on Iron and Steels
- テツ オヨビ タンソ コウ ノ ナイブ マサツ ソクテイ
この論文をさがす
抄録
The internal friction in iron and steels was measured as a function of temperature, using a torsion pendulum at about 1.9 cps. Vacuum-melted electrolytic iron with low nitrogen content (0.004%) exhibits, in addition to a Snoek damping peak, a stress-relaxation peak at about 500°C and 550°C respectively. However,the vacuum-melted electrolytic iron treated with wet hydrogen exhibits a stress-relaxation peak at about 500°C. The first peak manifested at about 500°C is a grain-boundary stress-relaxation peak, and the second peak at 550°C is the solid-solution peak accompanying the presence of nitrogen in solid solution in α-iron. Armco iron recrystallized at 650°C after cold drawing exhibits a pronounced solid-solution peak at about 570°C. The activation energy of the solid-solution peak in Armco iron is 64,000 cal/mol. The peak is characterized by a distribution of relaxation times. The peak decreases markedly by the precipitation of cementite at the grain interfaces. The peak is considered to be a grain-boundary peak for the solid-solution of carbon in α-iron. In annealed states, the Snoek damping peak in medium and high carbon steels cannot be detected, and a material recrystallized at 650°C after cold-drawing exhibits a smaller Snoek damping peak than the same material annealed at above A3−1. The Snoek damping peak in iron is markedly affected by A3 transformatiom.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 23 (7), 418-422, 1959
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681458594432
-
- NII論文ID
- 130007333562
- 40018257479
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9152919
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可