Al-Cu合金の析出におけるθ′相からθ相への変化の直接観察

DOI Web Site Web Site 被引用文献1件

書誌事項

タイトル別名
  • Direct Observation of Change from θ′ to θ Phase in Precipitation of an Aluminium-Copper Alloy
  • Al-Cu合金の析出におけるθ'相からθ相への変化の直接観察
  • Al-Cu ゴウキン ノ セキシュツ ニ オケル シータ ソウ カラ シータソウ エ ノ ヘンカ ノ チョクセツ カンサツ
  • Direct Observation of Change from θ′ to θ Phase in Precipitation of an Aluminium-Copper Alloy

この論文をさがす

抄録

Transmission electron microscopic studies on precipitation in thin foils of an Al-3.8%wt%Cu alloy have been carried out using a specimen heating attachment and a special 16 mm movie camera. The results obtained are as follows: (1) θ precipitates nucleate at the edge of some θ′ precipitates. θ′ precipitates with θ nucleus gradually grow, but the others having no nucleus gradually disappear. (2) Nucleation of θ phase is never observed in the matrix, except at grain boundaries or the edge of the foil. (3) Newly formed θ precipitates are not perfectly stable; i.e., some of them grow larger but the others shrink to disappear as ageing proceeds. (4) When the foil specimen is very thin, the movement of diffraction contours and their irregularities around precipitates are observed during the change from θ′ to θ phase. They may be due to strain produced by the volume change of precipitates. (5) Rough estimation of diffusion coefficient of copper in aluminium from the measurement of growth rate of θ precipitates gives the value of the same order, but to some degree larger than that obtained from the ordinary diffusion experiment in the bulk materials. (6) Although precipitation in thin foils of supersaturated solid solution at about 300°C appreciably differs from that in the bulk material in some cases, the sequence of precipitation from θ′ to θ phase in thin foils is nearly the same as that occurring in the bulk material.

収録刊行物

  • 日本金属学会誌

    日本金属学会誌 27 (12), 599-604, 1963