- Effect of Cold Working on Stress-Corrosion Cracking of Stainless Steels
- ステンレス コウ ノ オウリョク フショク ワレ ニ オヨボス レイカン カコウ ノ エイキョウ
この論文をさがす
抄録
An investigation was made of the effect of cold working on the susceptibility of seven austenitic stainless steels belong to AISI Type 304(or 304 L) to stress-corrosion cracking in high temperature NaCl solution (300°C, 500 ppm as Cl−) and in boiling 42%MgCl2 solution. The stress-corrosion was compared with the general corrosion in high temperature pure water and high temperature NaCl solution. These results are summarized as follows: (1) The carbon contents and heat treatments before cold working do not affect appreciably the susceptibility of stainless steel to the stress-corrosion cracking in high temperature NaCl solution. (2) The degree of cold working does not seem to have a direct relation to the susceptibility of stainless steel to the stress-corrosion cracking in high temperature NaCl solution and in boiling 42%MgCl2 solution. However, the ferrite transformed from the austenite by cold working decreases significantly the susceptibility of stainless steel to the stress-corrosion cracking in both solutions. (3) The general corrosion rate of uncracked specimens is higher than that of cracked ones.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 27 (11), 548-553, 1963
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681458605184
-
- NII論文ID
- 130007333580
- 40018258196
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153636
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可