- Compression Tests for Various White Irons (Studies on Alloy White Cast Iron (7th Report)
- シロ チュウテツ ノ アッシュク シケン
この論文をさがす
抄録
Compression tests were performed on as-cast and heat-treated specimens of the alloys Nos. 1∼12 in report No. 6. The summarized results were as follows: (1) As the hardness of primary crystal increased, the yielding stress increased from 30 to 140 kg/mm2, but was not affected so much by C% of alloys. (2) At about constant strain of 1%, the compressive stress increased almost in proportion to the hardness of the specimens, but at 0.3% strain the compressive stress varied markedly for the specimens having the same hardness. The factors causing this variation seemed to be the S, C contents, the melting and the casting conditions and the heat-treatment of the alloys. (3) The specimens having hardness of above 60HRC fractured vertically or were crushed to pieces, at about 1% strain and the stress of about 320 kg/mm2. On the other hand, the specimens below about 55HRC fractured on the plane about 45° to the compressed axes, at the stress of 160∼280 kg/mm2 and about 3∼30% strain.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 23 (9), 499-503, 1959
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681458623616
-
- NII論文ID
- 130007333608
- 40018257521
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9152961
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可