オーステナイト→マルテンサイト変態の安定化現象について

DOI Web Site Web Site

書誌事項

タイトル別名
  • Stabilization of Austenite-Martensite Transformation. (Sub-Zero Treatment of Quenched Steel (5th Report))
  • オーステナイト マルテンサイト ヘンタイ ノ アンテイカ ゲンショウ ニ ツイテ

この論文をさがす

抄録

The stabilization of retained austenite after partial transformation to martensite has been investigated using 1.12%C, 4.98%Ni steel. The stabilization degree was expressed by the temperature lag θ of transformation point or the stabilized austenite %δ. It was observed that the temperature lag θ is a function of aging time. In this steel, the following empirical equation expresses the relation between θ and aging time at room temperature: θ=52−48t−0.34 where θ is the temperature lag in centigrade degrees and t is the aging time in minute. It has been found that the recovery of martensite transformation occurred during subsequent cooling after aging in the early stage of stabilization, but did not occur in the last stage of it. Accordingly the correlation between θ and δ is not a linear relation. The stabilization proceeds very rapidly when the previously transformed martensite increases to more than 65%.

収録刊行物

  • 日本金属学会誌

    日本金属学会誌 23 (3), 156-160, 1959

    公益社団法人 日本金属学会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ