放電加工の際に生じた炭素鋼粉末のマルテンサイト変態

DOI Web Site Web Site

書誌事項

タイトル別名
  • Martensite Transformation of Carbon Steel Powders Produced by Electro-Spark Machining
  • ホウデン カコウ ノ サイ ニ ショウジタ タンソ コウフンマツ ノ マルテンサイト ヘンタイ

この論文をさがす

抄録

Fine particles of carbon steel containing 0.9 and 1.4% carbon were made by electro-spark machining, in which a simple R-C resonance circuit was used, the voltage being 100 volts, R 100 Ω and C 2 or 16 μF. The insulating liquid was transformer oil or ethanol. The size and structures of the produced particles were examined by means of electron microscopy and X-ray diffraction with the following results: The size was about 0.01 μ in diameter, which was independent of the condition of machining and of the carbon content. In the Debye-Scherrer photographs, a stronger but somewhat diffused pattern of austenite was seen while that of martensite was weaker compared with the case of bulk steels. This fact indicates a suppression of martensite transformation, which is interpreted to be due to the following two effects: The surface effect coming from the small particle size of about 0.01 μ, and the effect of the cooling with an extremely rapid cooling rate probably from a very high temperature as approximating boiling point of steel.

収録刊行物

  • 日本金属学会誌

    日本金属学会誌 23 (12), 728-731, 1959

    公益社団法人 日本金属学会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ