空気を含む水溶液中におけるニッケルの自己不働態化

DOI Web Site Web Site

書誌事項

タイトル別名
  • Self-Passivation of Nickel in Aerated Aqueous Solution
  • クウキ オ フクム スイヨウエキ チュウ ニ オケル ニッケル ノ ジコ フドウタイカ

この論文をさがす

抄録

The corrosion rate of nickel was measured in aerated sulfate solutions of various pH. An abrupt change of corrosion rate was found at aboult pH 5. In acidic region, the corrosion rate was nearly equal to the diffusion rate of dissolved oxygen and the spontaneous potential was less noble than the Flade potential. In alkaline solution, on the other hand, the corrosion rate was undetectablly small and the spontaneous potential was in the passive region. The polarization curve of nickel in acidic solution (pH=3.77) showed that the maximum dissolution current of iMmax in the active state, which can be measured in the solution saturated with pure nitrogen gas, was larger than the reduction current of dissolved oxygen iO. While, in neutral solution (pH=7.53), iMmax was smaller than iO. The critical state of iMmax=iO was found to be at about pH=5. It could be explained from the electrochemical standpoint that nickel is passivated by the reduction current of dissolved oxygen (O2+2H++4e→2OH−) only when |iMmax|<|iO|.

収録刊行物

  • 日本金属学会誌

    日本金属学会誌 23 (12), 725-728, 1959

    公益社団法人 日本金属学会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ