書誌事項
- タイトル別名
-
- Temperature and Orientation Dependence of the Plasticity of Magnesium Single Crystals
- マグネシウムタンケッショウ ノ ソセイ ニ オヨボス オンド ト ホウイ ノ エイキョウ
この論文をさがす
抄録
Plastic deformation in magnesium single crystals was investigated by tensile test at various temperatures (from room temperature to 400°C). The results obtained were as follows: (1) The critical resolved shear stress for basal slip is about 80 g/mm2 at room temperature, and about 60 g/mm2 at 200° and 400°C. (2) {10\bar12} twins occur in crystals for which χ\gtrsim57° at room temperature and in crystal for which χ=70° at 400°C, where χ is the angle between the basal plane and the stress axis. (3) {10\bar11}⟨11\bar20⟩ pyramidal slip occurs above 220°C, while any nonbasal slip is observed below 200°C. (4) The ductility develops remarkably above 250°C by the aid of the pyramidal slip. (5) In crystals for which χ\gtrsim35°, fracturing occurs nearly along the basal plane, while it occurs on {10\bar11} plane or other high index planes in crystals for which χ=5∼12°, below 230°C. (6) Above 250°C, fracturing occurs after necking caused by the pyramidal slip. (7) Crystals for which χ\gtrsim35° remarkably hardens by much kinking and bending at room temperature, while these kinking and bending are not observed at 400°C.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 23 (11), 649-652, 1959
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681458860928
-
- NII論文ID
- 130007333796
- 40018257329
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9152769
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可