- Effect of Chromium and Molybdenum on Magnetic Properties of High Permeability Iron-Aluminum Alloys
- コウドウジリツ Fe-Al ゴウキン ノ ジセイ ニ オヨボス Cr , Mo ノ テンカ コウカ ニ ツイテ
この論文をさがす
抄録
The effect of chromium and molybdenum on the magnetic properties of high permeability iron-aluminum (13∼16%) alloys was studied. The magnetic properties were measured after heating at 1000°C in hydrogen atomosphere and water quenching from 600°C.<BR>The results obtained are as follows:<BR>(1) The addition of 2∼4% molybdenum improves greatly the magnetic properties of Fe-Al alloys. The aluminum content which is required to exhibit the most favorable magnetic properties proportionally decreases with the increasing molybdenum content. The values of μ0>6000, μm>100000 and Hc<0.03 Oe are obtained in a wide composition range from 14.3 to 15.8%Al and, in particular, the 3%Mo-14.6%Al-Fe alloy has the maximum values: μ0=8000, μm=120000, Hc=0.020 Oe.<BR>(2) The addition of 1∼2% chromium slightly improves the magnetic properties, but 3∼4% chromium deteriorates.<BR>(3) The saturation induction decreases with increasing chromium and molybdenum contents.<BR>(4) Oil and air quenchings remarkably deteriorate the magnetic properties in all the specimens.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 28 (8), 457-460, 1964
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681459009152
-
- NII論文ID
- 40018258401
- 130007334009
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153841
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可