- Nakamura Fumitoshi
- Faculty of Engineering, Kansai University
-
- Saito Seizo
- Department of Science and Technology, Kinki University
-
- Okabayashi Kunio
- Faculty of Engineering, University of Osaka Prefecture
Bibliographic Information
- Other Title
-
- 真空度の摩耗におよぼす影響
- シンクウド ノ マモウ ニ オヨボス エイキョウ
Search this article
Abstract
The relation between vacuum degree and wear has been made clear in the range of the low frictional velocity, but that of the high frictional velocity is unknown.<BR>This study has been carried out using a specimen of carbon steel in the range of 760∼2×10−5 mmHg. The frictional velocity is 400 rpm (1.63 m/sec) and 1200 rpm (4.89 m/sec), and the normal load is 1 kg.<BR>The results obtained are as follows:<BR>(1) In the velocity of 400 rpm, the wear loss in the range of 760∼1 mmHg decreases with the increase of vacuum degree. However, it becomes almost constant beyond a certain high vacuum degree.<BR>(2) In the velocity of 1200 rpm, a seizure phenomenon was observed on the worn surface of the ring specimen and the wear loss of the rod specimen becomes the maximum at a vacuum of 10−1 mmHg.<BR>(3) The hardened patches are more effective in the wear resistance than the oxide film at the wear surface.
Journal
-
- Journal of the Japan Institute of Metals and Materials
-
Journal of the Japan Institute of Metals and Materials 28 (8), 465-470, 1964
The Japan Institute of Metals and Materials
- Tweet
Details 詳細情報について
-
- CRID
- 1390282681459010176
-
- NII Article ID
- 130007334011
- 40018258406
-
- NII Book ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL BIB ID
- 9153846
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed