- Relation between Directionality of Quenching-Deformation of Low Alloy Tool Steel and its Structure
- テイゴウキン コウグ コウ ノ ヤキイレ ワイ ノ ホウコウセイ ト ソシキ ト ノ カンレン ニ ツイテ
この論文をさがす
抄録
To investigate the effect of directionality on the quenching deformation of a low alloy tool steel (JIS SKS 3), the dimentional changes due to quenching and subsequent treatments were measured of the specimens forged at various forging ratios. Further, thermal dilatometric experiments and microscopic observation were carried out. The results are as follows. (1) There is no difference in quenching-deformation of as cast steels by the direction in which the specimens were cut out, but the linear expansion due to quenching was more marked in the transversal specimens of the steel forged at a forging ratio of 1.5 than the longitudinal ones. This shows that a slightly forged steel has directionality on quenching-deformation. (2) When the cylindrical specimens were quenched, they were deformed by the effect of the form of specimens and at the same time by the effect of directionality of the steel. The subsequent tempering or the sub-zero treatment does not change the ratio of length and diameter of the specimens. (3) The Ms point of the longitudinal specimen is 10°C lower than the transversal one. (4) The fibre structure of the steel consists of many fine layers containing alloying elements of different amounts, and the layers have different Ms points. It was concluded that anisotropy of the quenching-deformation of this steel depends on the above feature of the fibre structure.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 28 (8), 489-494, 1964
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681459020288
-
- NII論文ID
- 130007334020
- 40018258407
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153847
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可