- Creep of Ni-Al<SUB>2</SUB>O<SUB>3</SUB> Type Dispersion strengthened alloys
- Ni-Al2O3型分散強化合金のクリープ
- Ni-Al2O3ガタ ブンサン キョウカ ゴウキン ノ クリープ
この論文をさがす
抄録
The dependence of steady state creep rate on temperature and stress was investigated an Ni-Al2O3 type dispersion strengthened alloys containing 1∼5 wt% alumina as extruded. The activation energy of steady state creep was about 70,000∼90,000 cal/mol. Steady state creep rate was proportional to σn, where σ is the stress. The value of n, however, was 6∼12, being larger than 4 which was proposed theoretically by G.S.Ansell et al. on the annealed SAP type alloys.<BR>It is considered that their theoretical equation need not be essentially modified by the substitution of the stress σ−σ0 for σ using appropriately defined σ0.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 28 (9), 559-562, 1964
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681459045888
-
- NII論文ID
- 130007334049
- 40018258416
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153856
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可