- Influence of Thermomechanical Treatment on Strength of a Cu-21 mass%Ni- 5.5 mass%Sn Alloy
- Cu-21 mass%Ni-5.5 mass%Sn ゴウキン ノ キョウド エ ノ カコウ ネツ ショリ ノ エイキョウ
この論文をさがす
抄録
The effect of thermomechanical treatment on the strength of a Cu-21 mass%Ni-5.5 mass%Sn alloy was investigated. The alloy was cold-rolled to a 50% or an 80% reduction and then peak-aged at 400℃ (50R-A or 80R-A), or first peak-aged at 400℃ and then rolled to a 50% or an 80% reduction (A-50R or A-80R). The A-50R alloy exhibited a higher 0.2% proof stress σ0.2 of 1120 MPa and a higher tensile strength σu of 1200 MPa than the 50R-A alloy, and the A-80R alloy exhibited larger values of σ0.2=1200 MPa and σu=1310 MPa than the 80R-A alloy. The higher proof stress of the A-50R or A-80R alloy than the 50R-A or 80R-A alloy was ascribed to the higher dislocation density and the smaller deformation twin boundary spacing. The value of σu=1310 MPa for the A-80R alloy is considerably larger than those of commercial Cu-(20~22) mass%Ni-(4.5~5.7) mass%Sn alloys produced by cold rolling and subsequent aging.<br>
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 78 (9), 344-349, 2014
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681459522560
-
- NII論文ID
- 130004685001
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 025793393
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可