純クロムの延性におよぼすPrestrainの効果について

DOI Web Site Web Site

書誌事項

タイトル別名
  • Effect of Prestraining on the Ductility of Pure Chromium
  • ジュンクロム ノ エンセイ ニ オヨボス Prestrain ノ コウカ ニ ツイテ

この論文をさがす

抄録

The effect of prestraining on the ductility of pure chromium at room temperature were studied and the following results were obtained: (1) The room-temperature ductility of chromium containing 0.004% nitrogen, which is obtained by electrolysis of chromic acid solution, can be improved considerably by means of prestraining by rolling. The most effective working conditions are: Rolling reduction 0.75∼3% at rolling temperature of 400°C and 3∼8% at 500°C. (2) Needle-like precipitates, probably nitrides, are observed in electron micrographs of properly prestrained and ductile specimens after polishing and electrolytic etching. (3) The effect of prestraining is considered to be due to the decrease of dissolved nitrogen atoms caused by the precipitation of nitride. The details of the effect can be explained from the correlation between (i) the amount of prestrain which controls the distribution of lattice defects and the enhancement of nitrogen and (ii) the temperature of prestraining which controls the solubility and diffusion of solute nitrogen atoms.

収録刊行物

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ