Si-Cr-Mn鋼のオーステンパーによる相変化について

DOI Web Site Web Site

書誌事項

タイトル別名
  • On Phase Changes During Austempering of Si-Cr-Mn Steels (Metallographic Study on Austempering, 1st Report)
  • Si-Cr-Mn コウ ノ オーステンパー ニ ヨル ソウヘンカ ニ ツイテ

この論文をさがす

抄録

Phase changes during austempering of Si-Cr-Mn steels at 300° or 400° have been studied by means of dilatometric, microscopic and X-ray diffraction methods. The austempering was found to proceed in the following three stages. 1st stage: Supercooled austenite begins to transform into ferrite supersaturated with carbon, causing the enrichment of the rejected carbon atoms in the remaining austenite. 2nd stage: Carbide precipitates out within the ferrite and begins to coagulate. 3rd stage: The remaining austenite rich in carbon begins to transform into an aggregate of ferrite and carbide. However, in the austempering of about one hour, the isothermal transformation is interrupted prior to its completion. Due to the stoppage of the transformation in the process of its progression, the remaining austenite containing 1.0∼1.2%C and of up to 5∼20% in the amount is retained without transforming into other structural constituents. In such austempering, silicon in steels delays the progression of the transformation and results in retaining more amount of austenite in the austempered product.

収録刊行物

  • 日本金属学会誌

    日本金属学会誌 25 (3), 201-205, 1961

    公益社団法人 日本金属学会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ