- Internal Friction and Young’s Modulus in Malleable Cast Iron
- カタンチュウテツ ノ ナイブ マサツ ト ヤングリツ
- Internal Friction and Young’s Modulus in Malleable Cast Iron
この論文をさがす
抄録
Changes in internal friction and Young’s modulus with the graphitization of malleable cast iron were investigated. The effects of strain-amplitude, the structures of the matrix, the content of graphite, the size and the shape of the graphite nodules were described and discussed. In the as-cast state internal friction was quite low and no amplitude dependence was observed for strains of less than 10−5, while the Young’s modulus was comparatively high. As the specimens, however, were heated to graphitize, internal friction became higher and reached a final value at the end of the graphitization. On the contrary the Young’s modulus decreased by a considerable amount with the graphitization. In the graphitized state the internal friction showed a well-defined amplitude dependence, that is, it increases linearly with the strain-amplitude. By this observation, the cause of internal friction in annealed malleable cast iron is considered to be caused by the magneto-mechanical static hysteresis in ferrite. The notch effect of graphite nodules may cause a local stress concentration and bring about an increase in static hysteresis.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 25 (7), 448-452, 1961
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681459569280
-
- NII論文ID
- 130007334666
- 40018257957
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153397
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可