- On the Structure of W-Co Electrodeposits Obtained from Tartrate Bath
- ナンコウメン ジョウ ノ シュセキサンエンヨク カラ ノ W-Co メッキ ノ コウゾウ ニ ツイテ
この論文をさがす
抄録
The influence of bath composition and current density on the crystal structure, microscopic structure, W content, hardness and current efficiency of W-Co deposits obtained from tartrate bath was studied. The W content, the microscopic structure and the crystal structure of W-Co deposits were correlated with one another and could be classified into three groups with the increase of W/Co weight ratio in plating solution and of current density. The three groups were as follows: Group A) 20∼35 wt%W, angular microscopic structure, preferred orientation of hexagonal α Co solid solution exhibiting the (10\bar10) or the (10\bar11) plane being parallel to the surface; Group B) 36∼42 wt%W, intermediate microscopic structure, preferred orientation different from that in group A; Group C) 43∼52 wt%W, granular microscopic structure, diffused X ray diffraction pattern in the range of d=2.25 to 1.89 Å. The cause of this diffuseness of diffraction lines observed in high W deposits may be explained in terms of the increase of strain in α Co lattice owing to the supersaturation of W atoms in the lattice.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 25 (4), 292-296, 1961
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681459617408
-
- NII論文ID
- 40018257914
- 130007334743
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153354
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可