- On the Equilibrium Diagram of Fe-Ni-Si System and the Ternary Compound σ-Phase Appearing in This System. (Fundamental Research of Constant Permeability Alloys, 2nd Report)
- Fe-Ni-Siケイ ジョウタイズ ナラビニ センパーム ゴウキン ニ アラワレル 3ゲン カゴウブツ シグマソウ ニ ツイテ
- On the Equilibrium Diagram of Fe-Ni-Si System and the Ternary Compound σ-Phase Appearing in This System. (Fundamental Research of Constant Permeability Alloys, 2nd Report)
この論文をさがす
抄録
By means of microscopic observation as well as magnetic and dilatometric analyses, the constitution of ternary alloys of iron-rich Fe-Ni-Si system was investigated and its equilibrium diagram concerning solid phase reaction was determined. The σ-phase, reported on in the previous paper(1), was found to be ferromagnetic and formed by a peritectoid reaction α+γ→σ, having a maximum temperature at about 920°C, at an original composition of about 29%Ni, 11%Si and 60%Fe, corresponding to the chemical formula Fe11Ni5Si4, after solidifying through an eutectic reaction, Melt→α+γ. It was also found that the composition of a constant permeability alloy “Senperm” in this system, extends over such a region where it shows a homogeneous α-phase at higher temperatures and then precipitates σ-phase with lowering temperature owing to its solubility change; this fact seems to corroborate our reasonings in the 1st report.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 24 (8), 534-538, 1960
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681459859328
-
- NII論文ID
- 130007335103
- 40018257742
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153182
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可