書誌事項
- タイトル別名
-
- The Diffusion in the Iron-Chromium Alloy
- Fe-Cr ゴウキン チュウ ノ カクサン
この論文をさがす
抄録
The self-diffusion data in the b.c.c. phase of Fe-Cr alloys—the author’s data and others in the literatures—have been summarized. (1) The self-diffusion coefficients of chromium and iron, (2) the chemical diffusion coefficients, are shown as a function of composition in the temperature range from 950° to 1275°C. (3) D0 for self-diffusion of chromium has the order of 10−4 cm2/sec in pure chromium. D0 for chromium shows large variation with composition, with a maximum of 10+1 cm2/sec at about 70 at%Cr and a minimum of 10−1 cm2/sec in 30 to 40 at%Cr. The concentration dependence of D0 of the self diffusion for the iron has the same trend as for chromium, although the self-diffusion for iron has a maximum of 10+4 cm2/sec and a minimum of 10−1 cm2/sec. (4) The concentration dependence of the activation energy of the self diffusion for chromium and iron is qualitatively similar to that of D0. For chromium self-diffusion, it varies in the range from 48 kcal/g-atom (30 to 40 at%Cr) to 72 kcal/g-atom(about 70 at%Cr). For iron self-diffusion, it varies in the range from 50 kcal/g-atom to 90 kcal/g-atom. The mechanism of the diffusion in this system is discussed.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 25 (11), 698-702, 1961
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681459933568
-
- NII論文ID
- 40018257823
- 130007335209
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153263
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可