The Effect of Age-Hardening on the Rigidity Modulus and the Internal Friction in 17-7PH Stainless-Steel Wire
Bibliographic Information
- Other Title
-
- 17-7PH不銹鋼線の時効に伴う剛性率,比抵抗硬度および内部摩擦の変化について
- 17-7PH フシュウコウセン ノ ジコウ ニ トモナウ ゴウセイリツ , ヒ テイコウ コウド オヨビ ナイブ マサツ ノ ヘンカ ニ ツイテ
Search this article
Abstract
The change of the rigidity modulus, the electrical resistivity, the hardness and the internal friction following age-hardening were studied with 17-7PH stainless-steel wire containing 1.24%Al.The measurement were made on specimen of 0.65 mm diameter, using a torsion pendulum, a potentiometer and a micro-Vicker’s hardness tester. The results obtained were as follows: (1) The hardness of 17-7PH stainless-steel wire increased remarkably by aging at 400∼500°, but only slightly by aging at 100∼200°. (2) The electrical resistivity decreased in three temperature ranges of aging, namely, 150∼200°, 300∼450° and 500∼600°. (3) The rigidity modulus increased in the aging temperature range of 100∼250° and 400∼500°, but decreased by aging above 550°. (4) The internal friction of 17-7PH steel wire decreased remarkably by aging at 100∼300°, but increased again by aging at 550∼650°.
Journal
-
- Journal of the Japan Institute of Metals and Materials
-
Journal of the Japan Institute of Metals and Materials 25 (1), 34-36, 1961
The Japan Institute of Metals and Materials
- Tweet
Details 詳細情報について
-
- CRID
- 1390282681459940608
-
- NII Article ID
- 130007335222
- 40018257776
-
- NII Book ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL BIB ID
- 9153216
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed