- On the ε-Phase Formation in Solution-treated and Heated Hadfield Steel
- ヨウタイカ ショリ シタ コウMn コウ ノ カネツ ニ ヨル イプシロンソウ ノ セイセイ
- On the ε-Phase Formation in Solution-treated and Heated Hadfield Steel
この論文をさがす
抄録
The effect of isothermal heating on the ε-phase formation in solution-treated standard Hadfield steel was studied. When solution-treated Hadfield steel was heated isothermally at some temperature range, it precipitated a large quantity of grain-boundary carbides and pearlitic constituents. Consequently, the carbon content in the γ-phase decreased, then the γ-phase was transformed to ε-phase after the specimens were cooled to room temperature. The isothermal temperature range of steels containing the ε-phase at room temperature shaped a C-curve which has the nose of 500°×5 hr and extending over the temperature range of 450∼625°. This range corresponds to the range in which a large quantity of pearlitic constituents were precipitated. The existence of the ε-phase in steels at room temperature was observed in both the microstructure and the X-ray diffraction pattern. This ε-phase was transformed to the γ-phase when the specimens were heated at 200∼280°,and this transformation was confirmed as a remarkable expansion in the thermal dilatation curve.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 25 (1), 57-60, 1961
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681459943552
-
- NII論文ID
- 130007335228
- 40018257800
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153240
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可