- Observation of Electron-microscopic Structures of Stress-aged Mild Steel
- オウリョク ジコウ シタ ナンコウ ノ デンシ ケンビキョウ ソシキ ニ ツイテ
この論文をさがす
抄録
The electron-microscopic structure of mild steel stress-aged (strain-aged under definite mechanical stresses) at various conditions was examined. The change of structure caused by strain-aging, at 100°C and 200°C for predetermined length of time, was also examined for mild steel which had been stress-aged at various conditions. It was confirmed by electron-microscopic study that the strain aging of mild steel is accelerated without doubt by mechanical stresses imposed on the specimen during the strain-aging so that much more solute atoms in ferrite will be consumed during the stress-aging to produce a great number of fine precipitates. The stress-aged specimens did not show any significant structural change even when they were strain-aged. This means that, after the stress-aging, there is not so many solute atoms in ferrite as may contribute to strain-aging of mild steel. It may be possible to obtain a non-ageable mild steel by utilizing the stress-aging.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 25 (1), 68-72, 1961
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681459950976
-
- NII論文ID
- 130007335244
- 40018257785
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153225
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可