- Aging Behaviour of Be-Cu Alloys, Containing Ni with Special Emphasis on its Relation to Solution-treatment and Cold-working
- ニッケル オ フクム ドウ-ベリリウム ゴウキン ノ ヨウタイカ ショリ オンド , レイカン カコウ ト ジコウ トクセイ
この論文をさがす
抄録
The effects of the temperature of solution-treatment (700∼850°) as well as cold-rolling prior to aging treatment (30 and 80% in reduction percentage) on the aging characteristics of Be-Cu alloys, containing a small amount of Ni between 150° and 550°C were investigated by measuring the hardness and observing the microstructure. A lowering of the temperature of solution-treatment remarkably reduced he velocity and the degree of age-hardening, but the change in aging curves at the respective temperatures was found not to be in proportion to the change of quenching temperature. Cold-working generally reduced the degree of age-hardening, and especially such discontinuous changes as abnormal softening or two-steps hardening have been observed at about 250∼350°C. The rate of hardening was greater in as cold-worked specimens than as-quenched ones, in the range of low-temperature aging, but it became obscure at higher aging temperatures owing to the abnormal change mentioned above. The results were discussed in relation to the microstructures observed.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 25 (1), 15-19, 1961
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681459970176
-
- NII論文ID
- 130007335285
- 40018257784
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153224
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可