Mn-Ga系におけるDO<SUB>22</SUB>型合金とその磁気特性について

DOI Web Site Web Site 被引用文献2件

書誌事項

タイトル別名
  • On the DO<SUB>22</SUB>-Type Alloys in the Mn-Ga System and Their Magnetic Properties
  • Mn-Ga系におけるDO22型合金とその磁気特性について
  • Mn Gaケイ ニ オケル DO22ガタ ゴウキン ト ソノ ジキ トクセイ

この論文をさがす

抄録

Crystal structures and magnetic properties of Mn-21.0∼35.0 at%Ga alloys have been investigated by means of X-ray diffraction, thermal expansion and magnetic measurements. It has been found that a metastable phase is revealed in the face-centered tetragonal DO22-type alloys in the composition range of 23.5∼31.2 at%Ga when reheated at 350∼450°C after water-quenching from the γ-Mn phase.<BR>This metastable phase has lattice parameters a of 7.09∼7.18×10−10 m and axial ratios c⁄a of 1.816∼1.840. Both of the values increase wrth Ga concentration. These DO22-type alloys in the Mn-Ga system have coercive forces greater than 3.7×105 A/m and a magnetocrystalline anisotropy constant of about 1.4×106 J/m3.

収録刊行物

  • 日本金属学会誌

    日本金属学会誌 42 (5), 474-479, 1978

    公益社団法人 日本金属学会

被引用文献 (2)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ