- Damping Capacity of Gentalloy in the Fe-Co Alloys
- Fe Coケイ ゴウキン Gentalloy ノ ゲンスイノウ ニ ツイテ
この論文をさがす
抄録
The measurements of internal friction Q−1 under tensile loading and mechanical properties have been carried out on open-melted Fe-Co alloys containing 5∼25%Co subjected to annealing at 900∼1200°C. The value of Q−1 at a frequency of 0.3∼1.1 Hz first increases sharply to a maximum with an increase in maximum shear strain amplitude and then decreases gradually. The higher the annealing temperature and the Co content, the greater becomes Q−1. An Fe-25%Co alloy exhibits the highest Q−1 value of 75×10−3 when annealed at 1200°C for 1 h. When the measuring temperature becomes higher, the Q−1 value at first decreases from about 400°C and sharply increases after reaching a minimum in the vicinity of 550°C. Moreover, the Q−1 value decreases rapidly with an increase in external d.c. magnetic field. The mechanical strength of Fe-Co alloys increases considerably with Co content.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 42 (4), 337-340, 1978
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681460140032
-
- NII論文ID
- 130007335472
- 40002874098
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 1940234
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可