- タイトル別名
-
- Improvement of Strength by Thermo-Mechanical Treatment in Cu-Ti Alloys
- カコウ ネツ ショリ ニヨル Cu Ti ゴウキン ノ キョウド ノ カイゼン
この論文をさがす
抄録
The strengthening by thermo-mecanical treatment in both Cu-4%Ti and Cu-4%Ti-0.11%Zr alloys was studied by micro-hardness measurements, tensile tests, electron microscopy, and X-ray diffraction.<BR>The following conclusions were obtained.<BR>When the both alloys preaged at 450°C for various times were cold-rolled up to 90% and then annealed finally at 450°C for a short time, their strength was remarkably increased up to 1300 MPa in ultimate tensile strength.<BR>As the annealing temperature was lowered the annealing time required to obtain a maximum hardness by the final annealing was longer.<BR>The increment of hardness by the final annealing depended on the amount of cold rolling, and linear relationships existed between the increments in hardness by cold working and final annealing.<BR>When preageing time was increased, the increment in hardness by the final annealing was decreased to a minimum and then it was increased. The maximum value of the increment in hardness was obtained for the specimens with few supersaturated Ti atoms after preageing.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 42 (3), 275-280, 1978
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681460191104
-
- NII論文ID
- 130007335565
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 1935138
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可