- Structure and Magnetic Properties of Rapidly Solidified Strontium Ferrites
- キュウレイ ギョウコシタ ストロンチウム フェライト ノ ソシキ ト ジセイ
この論文をさがす
抄録
Amorphous formation regions for the pseudo-ternary SrO-Fe2O3-B2O3 system were investigated using melt spinning and water quenching techniques. The specimens were heat treated, and then examined to determine the composition and temperature ranges where the M-type ferrites precipitated, and the relationship between crystalline phases and magnetic properties was discussed.<BR>The amorphous formation region by melt spinning is restricted within the composition range of less than 60 mol%Fe2O3 and 60-70 mol%SrO, and that by water quenching within the composition range of less than 25 mol%Fe2O3 and more than 30 mol%B2O3.<BR>The region, where M-type ferrites are crystallized by heating, is divided into two: one is the area where the particle size and coercive force of M-type ferrite depend on cooling rate, and the other is the area where they are independent of cooling rate. In the former, the composition ranges are determined where fine M-type ferrite particles of high coercive force (higher than 320 kA/m (4 kOe)) precipitate from the heat-treated amorphous phases. Although the maximum coercive force of 560 kA/m (7000 Oe) is obtained in the latter, fine particles smaller than a superparamagnetic particle size are also formed.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 54 (1), 101-110, 1990
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681460211840
-
- NII論文ID
- 130007335602
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
- http://id.crossref.org/issn/00214426
-
- NDL書誌ID
- 3653968
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可