溶湯の直接圧延におよぼす板厚の影響

DOI Web Site Web Site 被引用文献1件

書誌事項

タイトル別名
  • Effect of Plate Thickness on the Direct-rolling of Molten Metals
  • ヨウトウ ノ チョクセツ アツエン ニ オヨボス イタアツ ノ エイキョウ

この論文をさがす

説明

The effect of plate thickness on the direct-rolling of molten metals of aluminium and its alloys was investigated, with the results summarized as follows:<BR>(1) As the plate thickness decreased, the direct-rolled plates showed the tendency to bend, which was especially remarkable in case of the alloys with a wide solidification range.<BR>(2) The upper limit of the direct-rollable speed related to the pouring temperature was not consistent with the low of inverse proportion to the plate thickness. Namely this limit became higher than the curve as the plate thickness became thicker and became lower as it became thinner.<BR>(3) Irrespective of the plate thickness, the texture in the pure aluminium annealed sheets made from plates at a higher direct-rolling speed was retained rolling texture {112}⟨111⟩, {112}⟨123⟩ and {100}⟨001⟩, while in the annealed sheets from plates at a lower direct-rolling speed the texture {110}⟨001⟩ strongly developed.

収録刊行物

  • 日本金属学会誌

    日本金属学会誌 34 (8), 780-785, 1970

    公益社団法人 日本金属学会

被引用文献 (1)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ