Composition of 3.5 GPa Grade Maraging Steels and the Thermo-mechanical Treatments
-
- Suto Hajime
- Department of Materials Science, Faculty of Engineering, Tohoku University
-
- Yin Zhong da
- Research Student of Tohoku University
Bibliographic Information
- Other Title
-
- 3.5 GPa級マルエージング鋼の組成と加工熱処理
- 3 5GPaキュウ マルエージング コウ ノ ソセイ ト カコウ ネツ ショリ
Search this article
Abstract
In order to obtain 3.5 GPa grade maraging steels, the chemical composition and the effect of thermo-mechanical treatments (TMT) including cold rolling have been investigated. From age-hardening experiments of various Mo-Co-Ni-Fe alloys, 14%Mo-(18 and 20)%Co-6%Ni alloys having superior hardness were selected. Tensile tests of these alloys bearing Ti and Al subjected to various TMT were carried out and the results were discussed observing the microstructures. Finally the materials having the hardness higher than Hv 950 (max. Hv 965) and tensile strength higher than 3.5 GPa (max. 3.70 GPa) were obtained by performing double direct quenchings after hot rolling from 1350°C inserted solution treatment at 1000°C for grain refinement, with subsequent cold rolling and aging.
Journal
-
- Journal of the Japan Institute of Metals and Materials
-
Journal of the Japan Institute of Metals and Materials 45 (6), 641-647, 1981
The Japan Institute of Metals and Materials
- Tweet
Details 詳細情報について
-
- CRID
- 1390282681460708480
-
- NII Article ID
- 40002875249
- 130007336474
-
- NII Book ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL BIB ID
- 2318171
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed