- Grain Boundary Reaction in a Cu-10 mass%Ni-8 mass%Sn Alloy
- Cu 10 massパーセント Ni 8 massパーセント Sn ゴウキン
この論文をさがす
抄録
The characteristics of the grain boundary reaction in a Cu-10 mass%Ni-8 mass%Sn alloy aged isothermally at 623 to 773 K after water quenching from 1123 K were investigated by optical and electron microscopic observations, hardness measurements and the X-ray diffraction methed. Results obtained are as follows:<BR>(1) The incubation periods were observed in the nodule growth curves, namely the nodule began to grow after the hardness of the matrix nearly reached a maximum value, and then engulfed the matrix entirely.<BR>(2) The pearlitic structure which consisted of the equilibrium α phase and the equilibrium γ phase [(Cu·Ni)3Sn] was observed in the nodule from the period of nodule formation, and the shape of the γ phase scarecely changed with progress of aging. The lattice parameter of the γ phase of an ordered fcc structure was 0.5940 nm.<BR>(3) The secondary pearlitic nodule containing γ precipitates larger than those in the primary nodule was observed on the prolonged aging after the completion of the primary grain boundary reaction.<BR>(4) The area fraction of the nodule, X, can be represented by Johnson-Mehl’s equation: X=1−exp(−btn), where t is the aging time and b and n are constants, and values 2.2∼2.6 were obtained as n.<BR>(5) The value of apparent activation energy for nodule growth was about 120 kJ/mol.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 46 (3), 307-312, 1982
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681460785920
-
- NII論文ID
- 130007336599
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 2444529
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可