The strain gauge factor K at room temperature, the electrical resistivity ρ at 20°C, its mean temperature coefficient Cf and the mean thermo-electromotive force relative to copper Emf in the temperature range 0 to 40°C have been measured with the cylindrical wires of Fe-Co-Mn alloys in a cold worked state of about 94% reduction. It has been found that the maximum value of K is 5.4 in Fe-Mn binary alloy containing 30%Mn and decreases gradually with increasing Co content, the non-magnetic γ phase alloys showing the values of more than 4.0. ρ of Fe-Co binary alloys increases monotonously with the addition of Mn, while their Emf shifts from a negative to a positive value with increasing manganese content. Cf of Fe-Mn or Fe-Co binary alloys decreases with increasing Co or Mn content, respectively. Fe-30%Co-45%Mn alloy which exibits the minimum Cf of 2.4×10−4 show K of 4.6, ρ of 98 μΩ-cm and Emf of +0.2 μV/°C.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 36 (10), 1040-1043, 1972
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681460800512
-
- NII論文ID
- 130007336626
- 40018255002
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 7610649
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可