- Effect of Niobium Additions on the Properties of New High Magnetic Permeability Alloys “Nimalloy” in the Nickel and Manganese System
- Ni-Mnケイ シン コウトウジリツ ゴウキン Nimalloy ノ トクセイ ニ オヨボス Nb テンカ ノ エイキョウ ニ ツイテ
- Effect of Niobium Additions on the Properties of New High Magnetic Permeability Alloys “Nimalloy” in the Nickel and Manganese System
この論文をさがす
抄録
Masumoto et al. previously discovered high permeability alloys near in composition to Ni3Mn which have an optimum degree of order, and named them “Nimalloy”. Much subsequent work has since been carried out so as to investigate the effects of various additive elements on the properties of nickel-manganese alloys as a result, the highest initial permeability of 76000 and the highest maximum permeability of 441000 have been obtained in the Ni-Mn-Fe-Cr system.<BR>The data on niobium additions to nickel-manganese alloys show that the initial and maximum permeabilities of nickel-manganese alloys at first increase gradually and later rapidly reach their maxima, and then decrease gradually. The alloy consisting of 77.55%Ni, 19.52%Mn and 2.93%Nb exhibits the highest initial permeability of 32500 when cooled at a rate of 240°C/hr from 900°C and reheated at 440°C for 41 hr, and the highest maximum permeability of 151000 when cooled at a rate of 240°C/hr from 900°C and reheated at 420°C for 80 hr. In the latter case, the alloy shows a coercive force of 0.0149 Oe and a magnetic hysteresis loss of 22.00 erg/cm3/cycle for the maximum magnetic induction of 5000 G, and an electrical resistivity of 50.4 μΩ-cm at 20°C.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 34 (1), 40-44, 1970
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681460855552
-
- NII論文ID
- 130007336724
- 40018256843
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 8372157
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可