- Unidirectional Solidification of 9%Ni Cast Steel in Rotary Magnetic Field
- 回転磁界型電磁攪拌場内における9%Ni鋳鋼の1方向凝固
- カイテン ジカイガタ デンジ カクハン バナイ ニ オケル 9パーセント
この論文をさがす
説明
The solidification structure of 9%Ni cast steel and the effect of electro-magnetic stirring on its structure and mechanical property were examined.<BR>9%Ni molten steel was poured into an exothermic mold and was solidified unidirectionally without stirring. Using the ingot, measurements were made of the primary and secondary dendrite arm spacings. Next, 9%Ni molten steel was solidified unidirectionally in a rotary magnetic field. The relation ship between primary arm spacing(S1; μm), secondary dendrite arm spacing(S2; μm) and average cooling rates (Va; K/s) was as follows:<BR>(This article is not displayable. Please see full text pdf.) <BR>And it was also confirmed that the as-cast ductility was greatly improved by this stirring, though this cast steel grade had no ductility as cast.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 52 (7), 694-700, 1988
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681460885760
-
- NII論文ID
- 130007336776
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 3196807
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可