Al-Co系合金の減衰能におよぼす冷間加工の影響

DOI Web Site Web Site 被引用文献1件

書誌事項

タイトル別名
  • Effect of Cold Working on the Damping Capacity of Al-Co Alloys
  • Al Coケイ ゴウキン ノ ゲンスイノウ ニ オヨボス レイカン カコウ ノ

この論文をさがす

抄録

The effect of cold working on the logarithmic decrement δ and the mechanical properties were investigated for Al-Co alloys containing 0.2 to 10.0%Co. δ and the rigidity modulus G were measured at room temperatures with an inverted torsion pendulum, and the tensile strength σt with an Instron-type tensile testing machine.<BR>The heat-treated alloys showed a slight increase in δ by the Co addition, but the value of δ remained as low as 9×10−3. At the same Co concentration the value of δ after furnace cooling was somewhat higher than that after water quenching. By cold working after heat-treatments, the value of δ considerably increased with increasing reduction in cross-sectional area, RA, for all alloys. With the increase in Co concentration, the value of δ after cold working steeply increased at first and above 1%Co, δ showed saturation for small RA or tended to decrease for large RA. Moreover, the alloys cold-worked after furnace cooling were higher in δ than those cold-worked after water quenching. The increment in δ by cold working was considered to be due to a remarkable increase in dislocation density.<BR>With increasing Co concentration, both G and σt of the heat-treated specimens increased but σt became almost constant above 2%Co. Cold working after heat-treatments gave a decrease in G and an increase in σt.

収録刊行物

  • 日本金属学会誌

    日本金属学会誌 53 (2), 227-231, 1989

    公益社団法人 日本金属学会

被引用文献 (1)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ