- Ti-Fe系,Ti-Cr系合金のミクロ偏析について
- Ti-Feケイ , Ti-Crケイ ゴウキン ノ ミクロヘンセキ ニ ツイテ
Search this article
Description
In order to understand a genetic trend of the microsegregation quantitatively measured by EPMA in transformation of titanium alloys, experiments on the effect of cooling rate from β phase and contents of the alloying element such as Fe and Cr were carried out on Ti-Fe and Ti-Cr binary alloys and on Ti-5Al-2Cr-1Fe alloy.<BR>As a result of the experiment and the examination with parameters such as the segregation index, the effective distribution coefficient and the β stabilizing rate, the genetic trend of the segregation for Fe was larger than Cr and there was a sort of a critical cooling rate under the effect of cooling rate from the β phase.<BR>Electron absorption images showed that this kind of segregation had a certain small area and distributed and scattered around. It was found that the less contents of β stabilizing elements, the larger the genetic trend of the microsegregation, and the trend was reduced with increasing degree of the β stabilizing in the alloys. It was also shown that the genetic trend of the microsegregation on 1 wt%Fe in Ti-5Al-2Cr-1Fe alloy was smaller than that on 1 wt%Fe in Ti-1Fe binary alloy, and that was in the other way on 2 wt%Cr in Ti-5Al-2Cr-1Fe and Ti-2Cr alloys.
Journal
-
- Journal of the Japan Institute of Metals and Materials
-
Journal of the Japan Institute of Metals and Materials 35 (6), 548-554, 1971
The Japan Institute of Metals and Materials
- Tweet
Details 詳細情報について
-
- CRID
- 1390282681461198976
-
- NII Article ID
- 130007337324
- 40018257202
-
- NII Book ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL BIB ID
- 8372516
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed