Ir-Mn-Sb系におけるCl<SUB>b</SUB>型金属間化合物とその磁性について

DOI Web Site Web Site 被引用文献1件

書誌事項

タイトル別名
  • On a Cl<SUB>b</SUB>-Type Intermetallic Compound in the Ir-Mn-Sb System and its Magnetic Properties
  • Ir-Mn-Sb系におけるClb型金属間化合物とその磁性について
  • Ir Mn Sbケイ ニ オケル Clbガタ キンゾクカン カゴウブツ ト ソ

この論文をさがす

抄録

Crystal structures and magnetic properties of Ir-Mn-Sb alloys were studied through X-ray and magnetic analyses. It has been found that the intermetallic compounds of the Clb-type structure exsist in the IrMn1+xSb system and forms a solid solution in the composition range of x=0.5∼0.8. IrMn1.5Sb and IrMn1.8Sb alloys of the Clb-type have lattice parameters of about 6.154 and 6.141 Å at room temperature, magnetic moments nB of 2.6 and 2.1 μB per Mn atom at absolute zero, and Curie temperatures Tc of 278 and 258 K, respectively. From the temperature dependence of reciprocal magnetic susceptibility 1⁄χg, these Clb-type alloys are expected to change from the ferromagnetism to the ferrimagnetism with increasing Mn content.

収録刊行物

  • 日本金属学会誌

    日本金属学会誌 40 (8), 812-816, 1976

    公益社団法人 日本金属学会

被引用文献 (1)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ