- Crystal Structure and Hardness of TiAl Phase Containing Zirconium
- Zr オ テンカシタ TiAlソウ ノ ケッショウ コウゾウ ト カタサ
この論文をさがす
抄録
The composition, crystal structure and hardness of TiAl(γ) phase contained in Ti-48-54 at%Al-0-12 at%Zr alloys annealed for 1 week at 1273 K have been studied. Obtained results are as follows: Soluble Zr atoms enter only into the Ti-sites of sublattice and increase only the a value of the lattice parameters, while, an increase of Al content increases only the c value. These anisotropic effects of the elements on the lattice parameters are attributed to the fact that covalent-like bonds are formed between the Ti atom layer and the Al layer. A region of a high degree of order shifts from (Ti1−xZrx)Al to Ti-rich side on the high Zr side. This cause is considered to be that Ti atoms play the same role as Al in the high Zr phase. A region of a low degree of order is located on the high Zr and high Al side, which is attributed to the existence of a degenerated ternary compound. The hardness depends not on the axial ratio c⁄a but on the degree of order. The solution hardening by Zr is observed only when the amount of the addition is small.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 51 (4), 278-284, 1987
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681461353088
-
- NII論文ID
- 130007337599
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 3133307
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可