- Effect of Prestraining on the Brittleness of Molybdenum
- モリブデン ノ ゼイセイ ニ オヨボス ヨ ワイ ノ コウカ ニ ツイテ
この論文をさがす
抄録
The effect of prestraining by tension on the brittleness of electron beam melted pure molybdenum was studied and the following conclusions were obtained:<BR>(1) The brittleness of the recrystallized pure molybdenum sheets can be improved considerablly below room temperature by prestraining about 5∼10% in the ductile range. The effect of prestraining increases with the amount of prestrain and changes with the temperature at which prestrain was given.<BR>(2) The prestrained specimens containing many edge dislocations show better ductility at low temperature than the prestrained specimens containing many screw dislocations.<BR>(3) Strain ageing due to interstitial impurities is negligible below 300°C.<BR>(4) As an important mechanisum, free dislocations and some Frank-Read sources introduced by the prestraining release the stress concentration when the prestrained specimens were tensile-tested at lower temperature, and the brittleness can be improved.<BR>(5) Ageing at 500°C after prestraining at 300°C decreases the ductility of prestrained specimens at low temperature. This is due to the dislocation locking caused by the interstitial impurities.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 37 (1), 88-93, 1973
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681461403008
-
- NII論文ID
- 40018255192
- 10011199352
- 130007337690
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 7610839
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可