- Nakai Hiroshi
- Department of Materials Science and Engineering, School of Science and Engineering, Waseda University
-
- Ichiba Mikiyuki
- Graduate Student, Waseda University
-
- Okada Ken
- Graduate Student, Waseda University
Bibliographic Information
- Other Title
-
- Ar-SO<SUB>2</SUB>雰囲気中におけるニッケル-クロム合金の高温腐食
- Ar-SO2雰囲気中におけるニッケルークロム合金の高温腐食
- Ar SO2 フンイキチュウ ニ オケル ニッケル クロム ゴウキン ノ コウ
Search this article
Abstract
The simultaneous attack of oxygen and sulphur on a range of Ni-Cr alloys containing 1-20(mass%)Cr has been investigated between 873 and 1173 K in PSO<SUB>2</SUB>=104 Pa atmosphere. Reaction kinetics was traced by using an automatic recording balance, and the scale structures were examined by metallography, scanning electron microscopy and microprobe analysis.<BR>The reaction kinetics was complex and classified into three groups of the temperature ranges. This complexity was owing to the sulphide formation and initial oxide properties. The corrosion kinetics followed more than two-step parabolic rate laws, but not followed by the simple single rate laws. Compared with pure nickel, the addition of up to 13%Cr at 918 K or below and at 1073 K or above, or 20%Cr at 918-1073 K has an effect on corrosion resistance.
Journal
-
- Journal of the Japan Institute of Metals and Materials
-
Journal of the Japan Institute of Metals and Materials 52 (1), 57-64, 1988
The Japan Institute of Metals and Materials
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390282681461707264
-
- NII Article ID
- 130007338233
- 40002876408
-
- NII Book ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL BIB ID
- 3170848
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed