ファンダメンタル・パラメータ法によるニッケル基耐熱合金の蛍光X線分析

DOI Web Site Web Site

書誌事項

タイトル別名
  • X-ray Fluorescence Analysis of Nickel-Base Heat-Resisting Alloys Using the Fundamental Parameter Method
  • ファンダメンタル パラメータホウ ニ ヨル ニッケルキ タイネツ ゴウキン ノ

この論文をさがす

抄録

The fundamental parameter (FP)-XRF analysis of ten alloying elements (Al, Ti, Cr, Mn, Fe, Co, Zr, Nb, Mo and W) in nickel-base heat-resisting alloys was performed with the XRF-11 program.<BR>One nickel-base alloy for multi-elements calibration standard was prepared by a vacuum arc melting method. The homogeneity test of alloying elements in the disk standard was performed by spark emission spectrochemical analysis. Consequently, the disk standard could be used for the FP-XRF analysis calibration. The chemical composition of the calibration standard was determined by the wet chemical analyses and inductively coupled phsma atomic emission spectrometry after ion-exchange separation.<BR>The spectral line overlaps were examined. The correction coefficients for the spectral line overlaps, that is, mMn,Cr, mCo,Fe, mNb,Mo and mMo,Zr, were 0.0004, 0.0003, 0.0004 and 0.0030 respectively. The accuracies for the determination of alloying elements with the proposed method obtained from fifteen standard reference materials were almost equal to those obtained by the correction method using theoretical alpha coefficients. The relative standard deviations (RSD) of repetitive seven measurements for the analytical values of the ten alloying elements were within about 1.5% with the exception of those for manganese (Mn; 0.01%, RSD; 6.08%) and tungsten (W; 0.06%, RSD; 6.69%).

収録刊行物

  • 日本金属学会誌

    日本金属学会誌 54 (5), 575-580, 1990

    公益社団法人 日本金属学会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ