- Some Problems on the Practical Use of a 3.5 GPa Grade Maraging Steel
- 3 5GPaキュウ マルエージング コウ ジツヨウジョウ ノ ニ サン ノ モ
この論文をさがす
抄録
In a previous paper, it was reported that the Miharisin’s 3.5 GPa grade maraging steel (8%Ni-14%Mo-18%Co-bal. Fe) had excellent fatigue strength, when it was prepared by a special basic melting and was subjected to thermomechanical treatments followed by cold rolling. In the present work, some problems on the practical use of this steel, that is, mechanical anisotropy, hydrogen embrittlement and the strength of welded joint were examined. The results are as follows:<BR>The typical texture as a BCC metal was developed by cold rolling, but the mechanical anisotropy was not so distinct. The conventionally heat treated steel is very sensitive to hydrogen embrittlement, but the cold rolling before age-hardening was effective to mitigate the embrittlement. Electron beam welding reduced the tensile strength from 3.5 GPa to 3.0 GPa, but it is recommended as an available welding process for this steel. The structures of weld metal and heat affected zones were observed by means of transmission electron microscopy.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 47 (7), 590-596, 1983
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681461904128
-
- NII論文ID
- 130007338574
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 2598960
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可