Fatigue Crack Propagation Characteristic and Fatigue Fracture Toughness in 780 MPa Grade High Strength Steel Weldments at Low Temperature
-
- Sato Kiyoshi
- Faculty of Engineering, Tohoku University
-
- Yokobori Takeo
- Faculty of Engineering, Tohoku University
-
- Igarashi Hiroshi
- Power Reactor and Nuclear Fuel Development Corp., Tokai
-
- Nishida Shin-ichi
- Yawata Works, Nippon Steel Corp.
-
- Masumoto Hiroki
- Yawata Works, Nippon Steel Corp.
Bibliographic Information
- Other Title
-
- 低温における780 MPa級高張力鋼溶接各部の疲労き裂伝ぱ特性および疲労破壊靭性
- テイオン ニ オケル 780MPaキュウ コウチョウリョク コウ ヨウセツ カ
- Fatigue Crack Propagation Characteristic and Fatigue Fracture Toughness in 780 MPa Grade High Strength Steel Weldments at Low Temperature
Search this article
Abstract
Fatigue test and fracture toughness test in 780 MPa grade high strength steel weldments in the temperature range from 98 K to room temperature were experimentally carried out. Both the tests were performed with a compact tension specimen by using a program-load-controlled 0.98 MN fatigue testing machine.<BR>Main results obtained are summarized as follows:<BR>(1) The fatigue crack propagation rate in the base metal shows a similar value in both the weld metal and HAZ.<BR>(2) The trend of fatigue crack propagation characteristic in weldments in the temperature range from 223 K to room temperature is in good agreement with the dislocation dynamics theory of fatigue crack propagation.<BR>(3) Fatigue fracture toughness, Kfc and fracture toughness, Kc in the base metal are larger than in both the weld metal and HAZ.
Journal
-
- Journal of the Japan Institute of Metals and Materials
-
Journal of the Japan Institute of Metals and Materials 47 (7), 596-602, 1983
The Japan Institute of Metals and Materials
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390282681461905280
-
- NII Article ID
- 130007338576
- 40002875623
-
- NII Book ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL BIB ID
- 2598968
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed