- Densities of LaCl<SUB>3</SUB>-MCl (M: Li, Na, K and Cs) Binary Melts
- 溶融LaCl3-MCl(M:Li,Na,KおよびCs)2成分系の密度
- ヨウユウ LaCl3 MCl M Li Na K オヨビ Cs 2セイブンケイ
この論文をさがす
抄録
Densities of LaCl3-alkali chlorides binary melts have been measured by the manometric method over the range of their liquidus temperatures to about 1200 K. The results obtained are summarized as follows:<BR>Density measured decreases with an increase in the content of alkali chloride for all the binary melts. Composition dependence of density shows a non-linear relation and the densities of mixtures at arbitrary compositions do not change in the order of the radius of alkali cation. Molar volume increases with an increase in the radius of alkali cation in the entire range of composition for all the binary melts. The molar volume of all the binary melt shows positive deviations from the additivity except the melt containing LiCl. The deviations become larger as the radius of alkali cation increases, and show a maximum at 50-60 mol% alkali chloride. Partial molar volumes of LaCl3 in each of the binary melts increase with increasing content of alkali chloride in the range of more than 40-50 mol% alkali chloride except the melt containing LiCl, and this tendency becomes stronger in the order of cationic radius. Expansion coefficient increases monotonically with increasing content of alkali chloride for all the binary melts and the value becomes larger in the order of cationic radius. It is found that the complex ions of LaCl4− and LaCl63− are co-existing in the melt containing LaCl3.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 51 (7), 630-636, 1987
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681461955584
-
- NII論文ID
- 130007338668
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 3145382
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可