- Fatigue Strength of Carbonyl Sintered Iron and Intergranular Fracture in Fatigue Test
- カーボニル ショウケツ テツ ノ ヒロウ ツヨサ ト ヒロウ カテイ ニ アラ
この論文をさがす
抄録
The fatigue strength of carbonyl iron compacts sintered at a temperature in the ferrite and austenite ranges and the intergranular fracture observed in the fatigue test were investigated.<BR>The results are as follows:<BR>(1) At the same compacting pressure, the fatigue strength of carbonyl iron compacts sintered for 3.6 ks in the temperature range between 1073 K and 1423 K is higher in ferrite and lower in austenite field.<BR>The endurance limit ratio obtained is in the range between 0.41 and 0.47.<BR>(2) The fatigue strength of specimens sintered isothermally at 1123 K and 1423 K increases gradually with the increase in the sintering time, except that of specimen sintered for 172.8 ks at 1123 K remarkably decreases.<BR>(3) The mode of fatigue fractured surface for specimens sintered at 1123 K is a mixed trans- and intergranular fracture type, while that for specimens sintered at 1423 K is mainly a trans-granular fracture type.<BR>The degree of intergranular fracture increases with the increase in the sintering time at 1123 K and with the decrease in carbon content.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 48 (1), 63-70, 1984
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681461987584
-
- NII論文ID
- 130007338724
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 2974074
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可