- The Beginning of Motion of Dislocations in Highly Perfect Copper Crystals
- コウ カンゼンド ドウ ケッショウ ニ オケル grown in テンイ ノ
この論文をさがす
抄録
Using an etch pit technique, which is applicable to distinguish between edge and 30°-screw dislocations, the shear stress τ0 necessary to move grown-in dislocations in highly perfect copper crystals is studied in relation to the condition of the crystal surface. The main results obtained are as follows: (i) Surface removal results in the remarkable reduction of τ0, which is more conspicuous in 30°-screw dislocation than in the edge one. (ii) Both edge and 30°-screw dislocations become very mobile at low stress levels with the reduction of partial pressure of O2 in the annealing atmosphere. (iii) Neither the surface-step formation in the motion of dislocations with screw character nor jogs along those with the edge character are found to have an important effect on τ0.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 43 (5), 364-371, 1979
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681462051840
-
- NII論文ID
- 130007338838
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 2052560
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可