- Effects of Crystal Orientation and Surface Conditions on Age and Quench Hardening of Beta Titanium-Molybdenum Alloy Single Crystals
- ベータガタ Ti Mo ゴウキン タンケッショウ ノ ジコウ オヨビ ヤキイレ
この論文をさがす
抄録
The age hardening of Ti-14 and 20 wt%Mo alloys at 623 K was investigated with their plate-like single crystal, bicrystal and polycrystal specimens in relation to crystal orientation and quenching strain induced by rapid cooling from 1223 K or 998 K for 20Mo and from 1223 K for 14Mo. The asquenched ω phase in single crystals showed higher hardness near the surface than that in the interior, when the specimen was mechanically abraded to a given depth. This phenomenon seemed to be influenced by solute oxygen and/or induced surface strain. The increase in age hardening in the interior, after a certain aging, kept up with that near the surface just under the contaminated layer (10-15 μm). The specimen with {110} surface hardened more quickly than that with {111} surface. The anisotropy of aging speed was verified with {320} and {211} surfaces of bicrystals (20Mo) for the quenching temperatures 1223 and 998 K. The effect of quenching temperature on age hardening was explained by the difference in the amount of quenched-in vacancies controlling the time period to the appearance of maximum hardness. After a long time aging, the interior of bicrystals showed a remarkable retardation of the age hardening.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 50 (10), 893-899, 1986
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681462239872
-
- NII論文ID
- 130007339181
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 3107975
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可