- On the Apparent Viscosity and Structure of Partially Solidified Al-Cu Alloys under Stirring
- 半溶融状態で攪拌したAl-Cu合金の組織とみかけ粘度
- ハン ヨウユウ ジョウタイ デ カクハンシタ Al Cu ゴウキン ノ ソシキ
この論文をさがす
抄録
Apparent viscosity of partially solidified alloys is expected to be extremely influenced by the size and morphology of crystals. An Al-5%Cu alloy was stirred during solidification with a paddle or a columnar rotor, and factors affecting the apparent viscosity and structure of the alloy slurry were investigated.<BR>The apparent viscosity (μ/Pa·s) of the slurry was approximated by the following equation as a function of the rotation speed (n/s−1) between rotor and crucible, the cooling rate (Vc/K·s−1) and the fraction solid (fs).<BR>(This article is not displayable. Please see full text pdf.) <BR>\oindentwhere A=1.8 (paddle) and 0.9 (columnar rotor).<BR>Primary crystals were broken into fine quasi-spherical particles by the stirring, while some of them coalesced into complicated particles in the slurry.<BR>A relationship was observed between the apparent viscosity and the particle coupling ratio Rn, that is, the ratio of the number (mm−2) of fine quasi-spherical primary particles to the number (mm−2) of complicated particles.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 48 (9), 936-944, 1984
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681462613632
-
- NII論文ID
- 130007339843
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 2997362
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可